Product Description of Ceramic Fiber Heat Proof Insulation Blanket:
Ceramic Fiber Blanket is an ideal heat proof thermal insulation, fire-proof and sound-absorbing material. The Ceramic Fiber Blanket is composed of long, flexible, interwoven fibers manufactured by the blown and the spun process yielding a strong, light weight, durable blanket for applications in a temperature range from 1100° C (2012° F ) to 1430° C (2600° F). The ceramic fiber blanket is completely inorganic and is needed to provide exceptional handling strength, used in a variety of heat processing applications.
Standard Dimension of Ceramic Fiber Heat Proof Insulation Blanket:
Density: 80-128Kg/m3.
Length: 3600-14000mm.
Width: 610mm.
Thickness: 6-50mm.
Advantages of Ceramic Fiber Heat Proof Insulation Blanket:
Low density and low thermal conductivity.
Resilience and resistance to thermal shock.
Excellent chemistry quality.
Flexible and easy to cut or install.
Our Services:
1). 7*24hours service.
2). Reply email in 10hours.
3). 10 production lines for short delivery time.
4). Support visit factory.
Product Application of Ceramic Fiber Heat Proof Insulation Blanket:
Ceramic Fiber Blanket is widely used for industrial furnace heat treatment, direct exposure to heat as furnace hot face lining, high temperature filter material, heat treatment insulation, and expansion joints.
Notes:
Common grade | 1100ºC(2012 ° F) |
Standard grade | 1260ºC(2300 ° F) |
High Pure grade | 1260ºC (2300 ° F) |
High Alumina grade | 1360ºC(2480 ° F) |
Zirconia grade | 1430ºC(2600 ° F) |
Technical Parameters of Ceramic Fiber Heat Proof Insulation Blanket:
Description | Common | Standard | High Purity | High Alumina | Zirconia | |
Maximum temperature (°C) | 1100 | 1260 | 1260 | 1360 | 1430 | |
Working Temperature (°C) | < 1000 | 1050 | 1100 | 1200 | 1350 | |
Color | white | white | white | white | white | |
Density (kg/m3) | 96-128 | 96-128 | 96-128 | 128-160 | 128-160 | |
Shrinkage(%)of heating 24 hours | -4 | -3 | -3 | -3 | -3 | |
(as density 128 kg/m3) | (1000°C) | (1000°C) | (1100°C) | (1250°C) | (1350°C) | |
Thermal conductivity (w/m.k)(Density 128 kgs/ m3)
| 0.09(400°C) | 0.09(400°C) | 0.09(400°C) | 0.12(600°C) | 0.16(800°C) | |
0.16(800°C) | 0.16(800°C) | 0.16(800°C) | 0.20(1000°C) | 0.20(1000°C) | ||
Tensile strength (MPa) (density as 128kg/m3) | 0.04 | 0.04 | 0.04 | 0.04 | 0.04 | |
Chemical composition(%) | AL2O3 | 44 | 46 | 47-49 | 52-55 | 39-40 |
AL2O3 & SIO2 | 96 | 97 | 99 | - | - | |
AL2O3 & SIO2 & ZrO2 | - | - | - | 99 | 99 | |
ZrO2 | - | - | - | 15-17 | 15-17 | |
Fe2O3 | <1.2 | <1.0 | 0.2 | 0.2 | 0.2 | |
Na2O & K2O | ≤0.5 | ≤0.5 | 0.2 | 0.2 | 0.2 |